Ngokusebenzisa asanda kwakhiwa izingoma impahla kanye elungiselelwe izinqubo ekhiqizako, ZP502 ihlanganisa izakhiwo eyaziwa omuhle ka zirconia futhi ithuthukisa lowehlukile ngokungeza zombala.
Lokhu kwaziswa ilungele izicelo ku amabhlogo zamazinyo multilayer futhi oyi-ukubopha. Lokhu indaba engase exutshwa zirconia ezimhlophe powder yethu yamazinyo ngokulungisa ifomula, ungase khiqiza phi multilayer noma pre-ukubopha zirconia block ofuna. Ngaphezu umbala ukuhumusha zako kakhulu, ZP502 Ubuye amandla kakhulu futhi bafake ukumelana.
umbala 1.Unique
sobuhle bayo 2.Highly
3.Superior ezingaphansi kolwandle ukuguga ukumelana
4.Excellent bio-kwedivayisi
powder izici | |
Ukwakheka | ZrO2 (HfO 2) / Y 2O 3= 97/3 Mol% |
Umbala sokuqukethwe | <1% |
Sio 2Okuqukethwe | <100 ppm |
Fe 2O 3Okuqukethwe | <100 ppm |
Na 2O sokuqukethwe | <50 ppm |
Cl -Okuqukethwe | <100 ppm |
surface Area | 10-14 m 2/ g |
Original Particle Usayizi | 30-50 NM |
Usayizi Distribution | D50 = 200 ~ 240nm |
Ubuningi sobala | > 1 g / cm 3 |
Properties of umzimba sintered | |
Ubuningi Sintered | > 6.0 g / cm 3 |
ubunzima | > 5.0 Mpa.m 1/2 |
Amandla ukugoba | > 1, 000 MPA |
ukuncipha | 1.23-1.24 |
* Usayizi Particle futhi D50 usayizi disribution kungenziwa egcizelele ngokusho izidingo zakho.