Product Description:
With cutting-edge nanotechnology and self-owned patents,Zirae ZP101S zirconia powder is manufactured by hydrothermal method with specially developed formula. ZP101S powder is more suitable for the production of mobile phone backcover. The sintered body has stronger bending strength and wear resistance by optimizing the process.
ZP101S can be widely used in exterior cellular phone covers and watch parts.
Features：
1.Excellent uniform dispersion
2.Ultra-fine particles
3.Highest flexural strength
4.High wear resistance
Chemical Composition:
| Chemical Composition | ZrO2 (HfO2)/Y2O3=97/3 mol% |
| Al2O3 Content | <2% |
| SiO2 Content | <100ppm |
| Fe2O3 Content | <100ppm |
| Na2O Content | <100ppm |
| Cl- Content | <100ppm |
| Surface Area | 13-16 m2/g |
| Particle Size | 30-50nm |
| Ignition Loss | <3% |
| Moisture | <0.5% |
| Apparent Density | >1g/cm3 |
| Size Distribution | D10 100-150NM |
| D50 200-240NM | |
| D90 400-600NM |
D50 size distribution can be customized according to your request.
Properties of sintered body:
| Sintered density | >6.0 g/cm3 |
| Fracture toughness | >5.0MPa.m1/2 |
| Flexural strength | >1000MPa |