Product Description:
Zirae ZP100C zirconia powder is basic grade ceramic material produced by coprecipitation method with the advantages of high strength and high wear resistance.
ZP100C powder is the most commonly used in ceramic parts and daily products.
Features：
1.High Strenth
2.Easy sintering
3.Good Fluidity
4.High wear resistance
Chemical Composition:
| Composition | ZrO2 (HfO2)/Y2O3=97/3 mol% |
| Al2O3 Content | <2% |
| SiO2 Content | <100ppm |
| Fe2O3 Content | <100ppm |
| Na2O Content | <100ppm |
| Cl- Content | <100ppm |
| Surface Area | 13-16 m2/g |
| Particle Size | 30-50nm |
| Whiteness | >90% |
| Ignition Loss | <3% |
| Moisture | <0.5% |
| Bulk Density | >1g/cm3 |
| Size Distribution | D10=100-150NM |
| D50=200-240NM | |
| D90=400-600NM |
Properties of sintered body:
| Sintered density | >6.0 g/cm3 |
| Fracture tougness | >4.0 MPa.m1/2 |
| Flexural strength | >1000MPa |