With cutting-edge nanotechnology and 33 patents, Zirae ZP100 zirconia powder is fine ceramic material produced by hydrothermal method with the advantages of excellent uniform dispersion,high strength and high wear resistance.
ZP100 can be widely used in fine ceramic parts and daily products.
1. High strength
2. High wear resistance
3. Excellent uniform dispersion
4. Low particle aggregation
Powder characteristics |
|
Composition | ZrO2(HfO2)/Y2O3=97/3 mol% |
Al2O3 Content | <2% |
SiO2 Content | <100ppm |
Fe2O3 Content | <100ppm |
Na2O Content | <100ppm |
Cl- Content | <50ppm |
Surface Area | 11-15 m2/g |
Original Particle Size | 30-50nm |
Whiteness | >90% |
Ignition Loss | <3% |
Moisture | <0.5% |
Apparent Density | >1g/cm3 |
Size Distribution | D10 100-150NM |
D50 200-240NM | |
D90 400-600NM |
Properties of sintered body | |
Sintered Density | >6.0g/cm3 |
Toughness | >4.0 Mpa.m1/2 |
Bending Strength | >1,000Mpa |
*D50 size distribution can be customized according to your requirements.