ZP502 Pink awọ Dental zirconium elo afẹfẹ Powder


ọja Apejuwe

ọja Tags

Nipasẹ rinle ni idagbasoke awọn ohun elo ti akopo ati ki o iṣapeye ẹrọ sii lakọkọ, ZP502 daapọ awọn ti mọ rere-ini ti zirconia ati ki o ndagba o yatọ si awọ nipa fifi pigments.

Yi awọn ohun elo ti jẹ apẹrẹ fun awọn ohun elo lori multilayer ki o si kọkọ-shaded ehín awọn bulọọki. Yi awọn ohun elo ti o le wa ni adalu pẹlu wa funfun zirconia ehín etu ati nipa Siṣàtúnṣe iwọn agbekalẹ, o le gbe eyikeyi multilayer tabi kọkọ-shaded zirconia Àkọsílẹ ti o fẹ. Ni afikun si awọn oniwe-o tayọ awọ Rendering anfani, ZP502 tun ni o ni o tayọ agbara ati yiya resistance.

1.Unique awọ

2.Highly aesthetics

3.Superior hydrothermal ti ogbo resistance

4.Excellent iti-ibamu

lulú abuda
tiwqn                                        ZrO2 (HfO 2) / Y 2Iwọ 3= 97/3 mol%                     
awọ akoonu <1%
SiO 2akoonu <100 ppm
Fe 2Iwọ 3akoonu <100 ppm
Na 2Eyin akoonu <50 ppm
Cl -akoonu <100 ppm
dada Area  10-14 m 2/ g
Original patiku Iwon           30-50 nm
iwọn Distribution D50 = 200 ~ 240nm
gbangba iwuwo > 1 g / cm 3

 

-Ini ti sintered body
Sintered iwuwo                                  > 6.0 g / cm                                                  
toughness > 5.0 Mpa.m 1/2
atunse Okun  > 1, 000 Mpa
shrinkage 1.23-1.24

* Patiku iwọn ati ki o D50 iwọn disribution le ti wa ni ti adani gẹgẹ bi awọn ibeere rẹ.