Physical PropertiesIndications
◆ Coping ◆ Inlay ◆ Onlay ◆ Anterior ◆ Veneer
Available in White Zirconia 98mm/95mm Puck
◆ 10mm 12mm 14mm 16mm 18mm 20mm 22mm 25mm
Chemical Composition
|
Y2O3 |
5.2-5.5 wt% |
|
AI2O3 |
0.05wt% |
|
SiO2 |
<0.002wt% |
|
Fe2O3 |
<0.002wt% |
|
Aging Properties |
Monoclinic Phase <20% |
|
Chemical Solubility |
≤2000hg.cm-2 |
|
Sintered Density |
6.0g/cm3 |
|
Flexural Strength |
≥800 Mpa |
|
Translucency |
>49% |
|
Fracture Toughness |
5Mpam1/2 |
|
Hardness(HV10) |
1250 |
|
Sintering Temperature |
1450°C |
Zirea UT multilayer Zirconia Block, The result is highly esthetic restorations with permanent strength and stability. Restorations are processed and fitted intraorally without additional cost using commercially available luting material.