Ka neng e sa tsoa ba le o hlophisitsoeng tse bonahalang le optimized dithulaganyo etsa thepa, ZP502 kopanyang ea tsebahalang thepa e ntle ea zirconia le develops mebala e fapaneng ka ho eketsa ka mebala.
boitsebiso bona ke loketseng bakeng sa ho dikopo ka likotoana tsa multilayer le pele ho di fifaditsweng di e meno. boitsebiso boo ka tsoakane le tšoeu zirconia meno phofo rona le ka ho fetola moralo, u ka hlahisa multilayer efe kapa efe kapa pele ho di fifaditsweng di e zirconia le literata u batla. Ho phaella ho babatsehang melemo ea eona mmala phetolelo, ZP502 boetse o na le matla a babatsehang le qhoaele hanyetsa.
1.Unique mmala
aesthetics 2.Highly
3.Superior hydrothermal botsofali hanyetsa
4.Excellent bio sebeletsana
litšobotsi tse phofo | |
Sebopeho | ZrO2 (HfO 2) / Y 2O 3= 97/3 Mol% |
mala Content | <1% |
Sio 2Content | <100 ppm |
Fe 2O 3Content | <100 ppm |
Na 2O Content | <50 ppm |
Cl facebook -Content | <100 ppm |
holim Area | 10-14 limithara 2/ g, |
Pele phatsa Size | 30-50 NM |
Size Kabo | D50 = 200 ~ 240nm |
totobala kitlano | > 1 g, / cm, 3 |
Properties tsa 'mele sintered | |
Sintered kitlano | > 6,0 g, / cm, 3 |
Toughness | >: 5.0 Mpa.m 1/2 |
kobang Matla | > 1, 000 Mpa |
Shrinkage | 1.23-1.24 |
* Phatsa boholo le D50 boholo disribution ka customized ho latela ditlhoko tsa hao.