Kudzera kumene anayamba nyimbo zakuthupi ndi wokometsedwa njira zotsimikizira, ZP502 Chili kudziwika katundu zabwino zirconia ndipo akufotokozera mumtundu powonjezera inki.
Nkhanizi ndi abwino ntchito pa midadada multilayer ndi Pre-shaded mano. Nkhanizi akhoza wothira woyera zirconia mano ufa wathu ndi kusintha njira, inu akhoza kupanga multilayer kapena Pre-shaded zirconia chipika mukufuna. Kuwonjezera kwambiri ubwino mtundu akuti ZP502 alinso mphamvu kwambiri ndipo avale kukana.
1.Unique mtundu
aesthetics 2.Highly
3.Superior Madziwo okalamba kukaniza
4.Excellent zamera-ngakhale
makhalidwe ufa | |
zikuchokera | ZrO2 (HfO 2) / Y 2O 3= 97/3 mol% |
mtundu zinthunzi | <1% |
SiO 2Timasangalala | <100 ppm |
Fe 2O 3Timasangalala | <100 ppm |
Na 2O zinthunzi | <50 ppm |
Cl -Timasangalala | <100 ppm |
pamwamba Area | 10-14 mamita 2/ g |
Choyambirira tinthu kukula | 30-50 nm |
kukula Kufalitsa | D50 = 200 ~ 240nm |
akuoneka kachulukidwe | > 1 g / masentimita 3 |
Katundu wa thupi sintered | |
Sintered kachulukidwe | > 6,0 g / masentimita 3 |
kulimba | > 5.0 Mpa.m 1/2 |
kupinda Mphamvu | > 1, 000 Mpa |
shrinkage | 1.23-1.24 |
* Tinthu kukula ndi D50 kukula disribution akhoza makonda malingana ndi zofuna zanu.