ZP502 Pink Agba Dental Zirconium oxide ntụ ntụ
Site e mepụtara ọhụrụ ihe onwunwe mebere na kachasị n'ichepụta Filiks, ZP502 agwakọta mara mma Njirimara nke zirconia ma na-amalite iche iche na agba site na-agbakwụnye pigments.
Nke a ihe onwunwe bụ ezigbo maka ngwa na multilayer na tupu-shaded eze blocks. Nke a ihe onwunwe ike weere na anyị na-acha ọcha zirconia eze ntụ ntụ na site n'ịgbanwe usoro, i nwere ike na-emepụta ọ bụla multilayer ma ọ bụ tupu-shaded zirconia ngọngọ na ị chọrọ. Ke adianade ya ndị magburu onwe agba nsụgharị uru, ZP502 nwekwara nwere magburu onwe ike na-eyi ndị na-eguzogide.
1.Unique agba
2.Highly aesthetics
3.Superior hydrothermal merela agadi na-eguzogide
4.Excellent bio-adabara
| ntụ ntụ e ji mara | |
| mejupụtara | ZrO2 (HfO 2) / Y 2O 3= 97/3 mol% |
| agba Content | <1% |
| SiO 2Content | <100 ppm |
| Fe 2O 3Content | <100 ppm |
| Na 2O Content | <50 ppm |
| Cl -Content | <100 ppm |
| n'elu Area | 10-14 m 2/ g |
| Original Particle Size | 30-50 nm |
| size Distribution | D50 = 200 ~ 240nm |
| o njupụta | > 1 g / cm 3 |
| Njirimara nke sintered ahụ | |
| Sintered njupụta | > 6.0 g / cm 3 |
| ike | > 5.0 Mpa.m 1/2 |
| ekwe Ike | > 1, 000 Mpa |
| shrinkage | 1.23-1.24 |
* Particle size na D50 size disribution nwere ike ahaziri dị ka gị chọrọ.